Hysil, composed of Hyrous Calcium Silicate, It is designed for use on systems operating upto 1100oC. It is inogranic, non-combustible, eco- friendly and meets the physical and property requirements of ASTM-C-533, BS-3958 PART II & IS Standard. Hil has a good flexural strength and water absorbent characteristics. HIL has a manufacturing facility / Plant in Dharuhera, Haryana, India.
900 x 600
600 x 450
600 x 300
600 x 150
450 x 300
Thickness
25 , 40 , 50
65 , 75 , 100
Half round, Curved segments for pipe lines of various dia. in thick-ness of 25, 40, 50, 65, 75 mm.
Other Sizes are also available on request.
| S.No. | Property | Units | H-800 Grade | H-1000 Grade | H-1100 Grade |
|---|---|---|---|---|---|
| Typical Values | Typical Values | Typical Values | |||
| 1 | Temperature, max service | Deg C | 800 | 1000 | 1100 |
| 2 | Average Bulk Density, Dry | Kg/m3 | 220-280 | 240-280 | 260-300 |
| 3 | Flexural Strength, (min.) | Kn/m2 | 300 | 350 | 600 |
| 4 | Compressive Strength,reduction in thickness not to exceed under a load of: I) 415 KN/m2, dry II) 170 KN/m2, after 18hrs immersion in water |
% % |
5.0 5.0 |
5.0 5.0 |
5.0 5.0 |
| 5 | Heat Resistance, under soaking I) Linear Reating Shrinkage (max.)- 12 Hours II) Loss In Mass (max.) III) Compressive Strength, reduction in thickness not to exceed under a load of 345 KN/m2(max.) |
% % % |
2 at 800oC 14.0 5.0 |
2 at 950oC 12.0 5.0 |
1.5 at 1050oC 10.0 5.0 |
| 6 | Thermal Conductivity at mean temperature (max.) 300oC 400oC 500oC 550oC |
W/m-K |
0.078 0.097 - - |
0.078 0.097 0.118 - |
0.076 0.090 0.110 0.114 |
| 7 | Moisture contents, by weight, (max.) | % | 5.0 | 5.0 | 5.0 |
| 8 | Alkalinity | pH | 8-11 | 8-11 | 8-11 |
* Tested in accordance with BS-874 Cold Face 40 deg.C. Also as per IS 9490, water calorimeter apparatus.